首页> 外文期刊>ISIJ International >Effects of Blast Furnace Representative Temperatures and Gas Compositions on Coke Reactivity
【24h】

Effects of Blast Furnace Representative Temperatures and Gas Compositions on Coke Reactivity

机译：Effects of Blast Furnace Representative Temperatures and Gas Compositions on Coke Reactivity

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相关主题

摘要

The effects of coke mineralogy on coke reactivity under conditions representative of the blast furnace were studied. Coke samples were reacted under coke reactivity index (CRI) like conditions (1 100 degrees C, 100% CO2) and at higher temperatures and atmospheres designed to replicate conditions lower in the blast furnace. The effects of the minerals on reactivity changed as the temperature increased and the atmosphere was modified. At the lower temperatures investigated (1 100-1 350 degrees C) with CO2 present in the gas, gasification of the coke by CO2 dominated. The effects of minerals in the coke on gasification by CO2 under these conditions were similar to their reported effects on reactivity in the CRI test. At the highest temperature investigated, (1 600 degrees C), with no CO2, the mineral-carbon reactions dominated. The main reaction was the reduction of the silica in the coke. These results show that when coke-gasification is dominant, CRI data can be related to conditions beyond the temperature and gas environment the data were obtained, to the higher temperatures and less oxidising conditions of the blast furnace. At higher temperatures, mineralcarbon reactions are dominant, and more data in addition to that of the CRI, may be required to understand coke behaviour in the blast furnace. IMDC and RMDC within the coke were identified with the aid of the CGA technique, and the changes in the carbon structures within the coke studied using Raman spectroscopy. The carbon structures within the coke became more graphitic at 1 600 degrees C, with the change in RMDC greater than that in IMDC.

著录项

获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号