首页> 外文期刊>ISIJ International >Hardening Behavior in Diffusion Zone of Fe-Mn and Fe-Cr Binary Alloys Nitrocarburized after Cold Working
【24h】

Hardening Behavior in Diffusion Zone of Fe-Mn and Fe-Cr Binary Alloys Nitrocarburized after Cold Working

机译：Hardening Behavior in Diffusion Zone of Fe-Mn and Fe-Cr Binary Alloys Nitrocarburized after Cold Working

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相关主题

摘要

To clarify the effect of dislocation on the precipitation behavior of nitrides, Fe-Mn and Fe-Cr binary alloys were deformed, nitrocarburized, and examined their hardening behavior. We measured the content of N in a diffusion layer and estimated the amount of alloy nitrides based on the measured N content. With the Fe-Cr alloy, the deforming have little effect on the hardness and CrN precipitation behavior. With the Fe-Mn alloy, the deforming contributes to increase in hardness with denser and finer Mn3N2 precipitation. Transmission electron microscopy observation shows CrN precipitates mainly by homogeneous nucleation but Mn3N2 precipitates mainly on dislocation. The thermodynamic calculation shows that substitutional alloy element (M) and N can form M-N clusters in Fe-Mn-N and Fe-Cr-N systems through phase separation of bcc lattice. Because Cr-N clusters have a higher nucleation driving force than Mn-N clusters, they can be formed by homogeneous nucleation. We evaluated the degree of the precipitation hardening and revealed that CrN has a larger hardening ability per unit precipitation amount than Mn3N2.

著录项

获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号