首页> 外文期刊>Nanotechnology >A novel high performance photodetection based on axial NiO/beta-Ga2O3 p-n junction heterostructure nanowires array
【24h】

A novel high performance photodetection based on axial NiO/beta-Ga2O3 p-n junction heterostructure nanowires array

机译：A novel high performance photodetection based on axial NiO/beta-Ga2O3 p-n junction heterostructure nanowires array

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相关主题

摘要

Axial NiO/beta-Ga2O3 heterostructure (HS) nanowires (NWs) array was fabricated on Si substrate by catalytic free and controlled growth process called glancing angle deposition technique. The field emission scanning electron microscope image shows the formation of well aligned and vertical NWs. A typical high resolution transmission electron microscope image confirms the formation of axial HS NWs consisting of beta-Ga2O3 NW at the top and NiO NW at the bottom with an overall length similar to 213 nm. A large photo absorption and also photoemission was observed for axial NiO/beta-Ga2O3 HS NW as compared to the NiO/beta-Ga2O3 HS thin film sample. Moreover, x-ray photoelectron spectroscopy analysis prove that there are higher oxygen vacancies with no deviation in electronic state after the formation of axial HS NW. Also, a high performance photodetector (PD) with a very low dark current of 6.31 nA and fast photoresponse with rise time and fall time of 0.28 s and 0.17 s respectively at +4 V was achieved using the axial NiO/beta-Ga2O3 HS NWs. The type-II HS p-n junction formation and efficient charge separation at the small wire axis also makes this design to operate in self-powered mode.

著录项

获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号