首页> 外文期刊>Nanotechnology >Coordination compound-derived Fe4N/Fe3N/Fe/CNT for efficient electrocatalytic oxygen evolution: a facile one-step synthesis in the absence of extra nitrogen source
【24h】

Coordination compound-derived Fe4N/Fe3N/Fe/CNT for efficient electrocatalytic oxygen evolution: a facile one-step synthesis in the absence of extra nitrogen source

机译：Coordination compound-derived Fe4N/Fe3N/Fe/CNT for efficient electrocatalytic oxygen evolution: a facile one-step synthesis in the absence of extra nitrogen source

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相关主题

摘要

By annealing an Fe(III)-coordination compound (Fe-CC), [FeCl3(Hbta)(2)] (Hbta = benzotriazole) in the presence of a carbon nanotube precursor (PCNT) template, an Fe4N/Fe3N/Fe/CNT heterostructure was successfully synthesized without an extra nitrogen source. The decomposition of the Hbta in Fe-CC under high-temperature annealing can produce carbon sheets and reduced graphene oxide (rGO), and the presence of CNTs can alleviate the stacking of the in situ-generated carbon materials. Meanwhile, iron nitride nanoparticles (NPs) can be anchored on the carbon sheets, and the anchoring effect efficiently prevents the agglomeration of NPs and increases the amount of active catalytic sites for the oxygen evolution reaction (OER). Fe4N/Fe3N/Fe/CNT shows an excellent OER activity with a Tafel slope of 63 mV dec(-1) as well as overpotentials of 121 (eta (10)) and 275 mV (eta (100)) at 10 and 100 mA cm(-2), respectively - far exceeding commercial RuO2 and other catalysts. Density functional theory calculations show that the excellent OER performance of Fe4N/Fe3N/Fe/CNT is associated with the Fe4N/Fe3N heterojunction, which can improve the electron conductivity and boost the electron transfer from N to Fe. The Fe4N/Fe3N/Fe/CNT catalyst exhibits long-term OER activity during 100 h of electrolysis at 20 mA cm(-2). This is related to the dual coatings of the in situ-generated thin carbon shell and few-layered rGO on the surface of the iron nitride NPs, which can protect the fast leaching of iron nitride during the OER process. Furthermore, the effects of the annealing temperature, the PCNT template and the heating rate on the calcined products were investigated.

著录项

获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号