首页> 外文期刊>Journal of Applied Polymer Science >Properties of polyamide 6/multiwalled carbon nanotubes composites: The influence of processing methods
【24h】

Properties of polyamide 6/multiwalled carbon nanotubes composites: The influence of processing methods

机译：Properties of polyamide 6/multiwalled carbon nanotubes composites: The influence of processing methods

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相关主题

摘要

The objective of this work was to elucidate the influence of shear rates on the properties of polyamide 6/multiwalled carbon nanotube (PA6/CNT) composites which was realized by adopting different types of processing methods that feature different orders of magnitude in shear rates, such as compression molding (CM, similar to 0 s(-1)), conventional injection molding (CIM, similar to 10(2) s(-1)) and microinjection molding (mu IM, similar to 10(5) s(-1)). Electrical conductivity (sigma) results indicated that the prevailing high shearing conditions in injection molding was unfavorable for the formation of intact filler network, thereby resulting in a much lower sigma than CM counterparts. Moreover, the sigma of PA6/CNT micro-parts was higher than that of CIM macroparts when the filler content was less than 5 wt%, otherwise the sigma of CIM macroparts prevailed over that of mu IM counterparts. A better filler distribution was observed when PA6/CNT composites were processed under higher shearing conditions, as corroborated by SEM. In addition, CNTs were preferentially aligned along flow direction and a higher degree of CNT orientation was expected with increasing shear rates, as confirmed by Raman spectral analysis. The tensile strength of injection molded PA6/CNT samples increased with increasing filler concentrations, and the more preferential orientation and better distribution of CNT were considered to be the contributing factors. The comparative study of the properties of PA6/CNT composites that processed using different methods was important for their practical applications in industrial sectors.

著录项

获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号