首页> 外文期刊>Journal of Applied Polymer Science >Vacuum formed bio-based composite materials using polyolefin and thermally modified wood powder
【24h】

Vacuum formed bio-based composite materials using polyolefin and thermally modified wood powder

机译：Vacuum formed bio-based composite materials using polyolefin and thermally modified wood powder

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相关主题

摘要

For climate and sustainability reasons, there is an interest and incentive to produce plastic and rubber products with increased content of a bio-based component, preferably existing as an industrial by-product, for example, wood powder/sawdust. There are many studies on the making of wood-plastic composites, but hitherto very few consider vacuum forming as a processing technique, especially considering a biofiller. Here, the properties of a vacuum formed composite with thermally modified wood powder (with reduced water uptake) and a very ductile polyolefin, was reported. Surprisingly, even at a 15 wt% filler content, the composite remained ductile (extensibility of ca. 30%). The water uptake increased with increasing content of wood powder, but was never more than 5%. The water sorption kinetics indicated that the wood powder did not form a percolated continuous path through the material for easy access to the water, which led to a low water diffusivity (ca. 2 x 10(-10) cm(2) s(-1)). The calorimetric data showed that the biofiller, overall, did not affect the melting and crystallization behavior of the polymer matrix, nor the observed glass transition temperature. To conclude, vacuum forming was shown to be a viable technique for composites with a very ductile/elastic matrix and stiff fillers.

著录项

获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号