首页> 外文期刊>Journal of Applied Polymer Science >Influence of alkaline delignification on moisture uptake behavior and bonding enthalpies of hemp
【24h】

Influence of alkaline delignification on moisture uptake behavior and bonding enthalpies of hemp

机译：Influence of alkaline delignification on moisture uptake behavior and bonding enthalpies of hemp

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相关主题

摘要

Raw hemp fibers are alkaline delignified to evaluate the effect of lignin on the moisture uptake behavior of hemp. Samples are subjected to moisture absorption/desorption isotherms from 5% to 95% relative humidity at three different temperatures (15, 25, and 35 degrees C). The sorption ratio between delignified and untreated hemp is lowered by 25%. Hysteresis makes evident the greater influence of lignin on moisture binding at low relative humidity while at high relative humidity, cellulose plays the most important role. The GAB, Hailwood-Horrobin and Dent models are fitted to absorption/desorption isotherms. Delignification and temperature decrease the size of the monolayer. The energy constants of the monolayer differ according to the model used. Lignin causes great differences between absorption and desorption. The greater the temperature is, the lower the monolayer energy constant. The energy constants of the multilayer are identical for the three models, showing a greater range of variation in delignified samples than in the untreated samples. Based on primary and secondary energy constants, bonding enthalpies are determined. Estimations in desorption show higher correlation coefficients with the energy constants, which enables to conclude that measures in desorption better explain the effect of delignification on the water uptake behavior of hemp.

著录项

获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号