首页> 外文期刊>Journal of Applied Polymer Science >Acrylate polymer prepared by dispersion polymerization and its crude oil emulsion demulsification performance
【24h】

Acrylate polymer prepared by dispersion polymerization and its crude oil emulsion demulsification performance

机译：Acrylate polymer prepared by dispersion polymerization and its crude oil emulsion demulsification performance

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相关主题

摘要

The development of a new crude oil emulsion demulsifier to replace the block polyether has always attracted attention. In this article, a novel crude oil emulsion demulsifier was prepared by dispersion polymerization using a mixture of ether and water as the dispersion medium and acrylate, methacryloxyethylthrimethyl ammonium chloride (DMC), and acrylamide as the comonomers. Taking the stability and demulsification performance as the index, the effects of acrylate type, ether/water mass ratio, monomer mass ratio, monomer concentration, initiator type, ether type, and reaction temperature on the polymerization results were investigated. The experimental results showed that when the acrylate was butyl acrylate (BA), the mass ratio of BA to DMC was 1:1, and dispersion medium was the mixture of dipropylene glycol methyl ether and water (ether/water mass ratio 1.5:1), monomer concentration was 20 wt%, initiator was V50, reaction temperature was in range of 50 to 55 degrees C, and polymerization reaction was 10 h, the product P (BA-DMC-AM) had a good demulsification performance for the crude oil emulsion (crude oil density 0.9625 g/cm(3), water content in emulsion 50%). When the dosage of P (BA-DMC-AM) was 200 mg/L and the temperature was 75 degrees C, its dehydration was higher than 90% after demulsification for 4 h. This efficiency was similar with the block polyether demulsifier BH133. In addition, interfacial properties showed that P (BA-DMC-AM) can adsorb onto the oil-water interface and reduce the strength of W/O interfacial film, thereby achieving demulsification.

著录项

获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号