首页> 外文期刊>Journal of manufacturing processes >Microstructures and mechanical properties of TIG welded Al-Mg2Si alloy joints
【24h】

Microstructures and mechanical properties of TIG welded Al-Mg2Si alloy joints

机译：Microstructures and mechanical properties of TIG welded Al-Mg2Si alloy joints

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相关主题

摘要

In this paper, the microstructures and mechanical properties of tungsten inert gas (TIG) welded joints were studied. Three zones were formed in these joints: a heat-affected zone (HAZ), a partial melting zone (PMZ) and a fusion zone (FZ). In the FZ, the microstructure consisted of only alpha-Al and eutectic Mg2Si. The alpha-Al segregation phenomenon occurred when the welding current increased from 125 A to 135 A. The low-angle grain boundaries (LABs) found in the base material (BM) transformed into high-angle grain boundaries (HABs) in the FZ. The texture of the BM was concentrated in three specific preferred orientations, whereas the texture was eliminated in the FZ. The hardness in the FZ was 45 % higher than that in the BM. The eutectic Mg2Si phase in the welded joints became fine and dense, and the needle-like beta '' phase in the BM was replaced by a high density of fine precipitates, which led to an increase in hardness. The ultimate tensile strength (UTS) and elongation of the joints welded at 125 A were lower than those of the BM and the joints welded at 135 A. Furthermore, no cracks were generated in the joints after multiple thermal shocks.

著录项

获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号