首页> 外文期刊>Corrosion Reviews >The corrosion behavior and cracking susceptibility of the disbonded coating in the X80 steel pipeline by theoretical simulations and experimental measurements
【24h】

The corrosion behavior and cracking susceptibility of the disbonded coating in the X80 steel pipeline by theoretical simulations and experimental measurements

机译：The corrosion behavior and cracking susceptibility of the disbonded coating in the X80 steel pipeline by theoretical simulations and experimental measurements

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相关主题

摘要

The corrosion behavior and cracking suscepti-bility of the disbonded coating in the X80 steel pipeline were investigated by different methods. The oxygen con -tent in the trapped solution decreased rapidly with the formation of an airtight disbonded area. The airtight system affected the electrode reaction process, resulting in the inhibition of corrosion in the center of the disbonded area and the more refined surface finish of the sample. The bottom of the disbonded area underwent a relatively intense and accelerated corrosion reaction controlled by the diffusion process. The cracking susceptibility of the X80 steel firstly decreased and then increased in the pointing direction.

著录项

获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号