Pilot scale production and evaluation of mechanical and thermal properties of P(3HB) from Bacillus megaterium cultivated on desugarized sugar beet molasses

机译：Pilot scale production and evaluation of mechanical and thermal properties of P(3HB) from Bacillus megaterium cultivated on desugarized sugar beet molasses

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相关主题

摘要

Abstract Production of poly[(R)‐3‐hydroxyalkanoate] (PHA) biopolyesters must become more cost efficient in order to be competitive with conventional plastics as well as other bioplastics. This study introduces a simple and reproducible large‐scale production process of poly(3‐hydroxybutyrate) P(3HB) with Bacillus megaterium based on desugarized sugar beet molasses and compares its material properties with commercially available types of PHA. A repeated batch cultivation system was evaluated in 1.2 L bioreactors and could be maintained for at least six cycles without a decrease in process stability, yielding a concentration of 20.4 g/L cell dry mass and 12 g/L P(3HB) per average process cycle. Feasibility of P(3HB) production was demonstrated at 500 L pilot scale to provide sufficient amounts of product for the determination of mechanical and thermal polymer properties. A volumetric productivity of 0.2 g L−1 h−1 was achieved. The resulting polymer exhibited a high tensile modulus of 3.73 GPa and tensile strength of 38.5 MPa. Despite a lower ductility and Vicat softening temperature, the properties of the recovered P(3HB) are comparable to commercial grade P(HB)HV polymers.

著录项

获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号