Experimental studies of fracture and fatigue crack growth in dissimilar metal welded joints of nickel-based superalloys: Cracks oriented along the weld

机译：Experimental studies of fracture and fatigue crack growth in dissimilar metal welded joints of nickel-based superalloys: Cracks oriented along the weld

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相关主题

摘要

Nickel-based superalloys, Inconel 718 and Nimonic 80A, were welded without any interlayer for Blisk manufacturing in aerospace industries. Fracture toughness and fatigue crack growth rate of the dissimilar metal welded joints were experimentally studied to confirm their structural integrity. Cracks were oriented in and along the weld. Base metals, Inconel 718, and Nimonic 80A differ in yield strength but have the same modulus of elasticity. Electron beam welding was used to butt weld Inconel 718 to Nimonic 80A. J resistance curve ( J vs. crack extension) was experimentally found to determine the elastic–plastic fracture toughness. The welded specimens showed lesser fracture toughness and higher crack growth rates than base metals. An increase in load ratio resulted in an increase in fatigue crack growth rate in the high Δ K region and a decrease in Δ K_(th) _(.)Fractography studies confirmed linear elastic and plane strain fracture all along the fatigue crack growth rate path except for the final fracture with plane stress.

著录项

获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号