Permanent Strength of Interstitial-free Steel Processed by Severe Plastic Deformation and Subsequent Annealing

Koizumi Takayuki; Takahashi Tomoki; Kuroda Mitsutoshi

首页> 外文期刊>ISIJ International >Permanent Strength of Interstitial-free Steel Processed by Severe Plastic Deformation and Subsequent Annealing

【24h】

Permanent Strength of Interstitial-free Steel Processed by Severe Plastic Deformation and Subsequent Annealing

机译：Permanent Strength of Interstitial-free Steel Processed by Severe Plastic Deformation and Subsequent Annealing

获取原文

获取原文并翻译 | 示例

掌桥外文数据库（机构版） >>

开具论文收录证明 >>

文献代查 >>

页面导航

摘要
著录项
相关主题

摘要

The permanent strengths of interstitial-free (IF) steels with different grain sizes and dislocation densities processed by severe plastic deformation (SPD) and subsequent annealing are systematically investigated. Permanent strength, which is athermal and time-independent, corresponds to the fundamental capability to bear stresses caused by external forces. Sufficiently long-time (24 h) stress relaxation tests were carried out and experimental stress-relaxation time relationships were extrapolated to estimate the permanent strength that remained after an infinite time passed. The flow stresses observed in standard uniaxial tension tests increased with repeated SPD processes, and the fraction of permanent strength to the observed flow stress was mostly above 65%. The permanent strength also increased with repetition of SPD processes, and subsequent low-temperature annealing further augmented the permanent strength. During SPD processes, the dislocation-related strengthening was dominant, while the grain-size-related strengthening was minor, i.e., the Hall-Petch relation does not hold. On the other hand, after low-temperature annealing, the grain-sizerelated strengthening became dominant, quickly replacing the dislocation-related strengthening. In a coarsegrain region, the grain-size-related strength was consistent with the classical Hall-Petch relation. It was confirmed that the original Hall-Petch relation holds only in the coarse-grain region and it indicates "softening with grain coarsening due to annealing", not "strengthening by grain refinement due to SPD".

著录项

来源
《ISIJ International》 |2023年第1期|179-189|共11页
作者
Koizumi Takayuki; Takahashi Tomoki; Kuroda Mitsutoshi;
展开▼
作者单位

Tokyo Coll;

Yamagata Univ;

展开▼
收录信息美国《科学引文索引》(SCI);美国《工程索引》(EI);美国《生物学医学文摘》(MEDLINE);
原文格式 PDF
正文语种英语
中图分类黑色金属材料;
关键词
structural metals; athermal strength; strain-rate sensitivity; stress relaxation; severe plastic deformation; Hall-Petch relation; strain hardening; HALL-PETCH RELATIONSHIP; ULTRAFINE-GRAINED ALUMINUM; HIGH-PRESSURE TORSION; KOCKS-MECKING MODEL; MECHANICAL-PROPERTIES; STRESS-RELAXATION; TEMPERATURE CREEP; ROOM-TEMPERATURE; YIELD-STRESS; STRAIN-RATE;

Permanent Strength of Interstitial-free Steel Processed by Severe Plastic Deformation and Subsequent Annealing