首页> 外文期刊>Journal of polymers and the environment >A Strategy to Achieve the Inherently Flame-retardant PA56 by Copolymerization with DDP
【24h】

A Strategy to Achieve the Inherently Flame-retardant PA56 by Copolymerization with DDP

机译：A Strategy to Achieve the Inherently Flame-retardant PA56 by Copolymerization with DDP

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相关主题

摘要

Abstract As a bio-based polyamide, polypentamethylene adipate (PA56) is restricted in many fields due to its flammability. In this research, flame-retardant PA56 copolymers (FRPA56s) were designed and successfully synthesized with the introduction of 9,10-dihydro-10-[2,3-di(hydroxy carbonyl)propyl]-10-phosphaphenanthrene-10-oxide (DDP) unit. The thermal properties, thermal degradation and flame behavior of the resultant copolymer were investigated by DSC, TGA, LOI, UL-94 and cone calorimeter tests, respectively. Compared to PA56, the peak value of heat release rate and total heat release of FRPA56 containing 1.2?mol% DDP decrease by 35% and 19%, respectively, indicating the high flame-retardant efficiency of DDP. It is also found that FRPA56 with only 1.0?mol% DDP passes V-0 grade in the UL-94 test while its thermal performance is almost the same as homopolymer PA56. The pyrolysis products in both the condensed and gas phases were further systematically analyzed by SEM, Raman, FTIR, X-ray photoelectron spectroscopy and TGA-GC/MS. The flame-retardant mechanism was also proposed for FRPA56s.

著录项

获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号