Four new oligo(azine)s were synthesized from dimethyldiphenylsilane and tetraphenylsilane core-based dialdehydes and hydrazine by high-temperature polycondesation and proposed as materials for optoelectronic applications. The oligo(azine)s were characterized by EA, FT-IR, and NMR. Although most of samples were poorly soluble, TPS-containing PAZ-4 was soluble in aprotic polar solvents. According to SEC and FT-IR studies, the samples were oligomers with up to five repeating units long. TGA showed highly stable samples with TDT10% over 420 degrees C except for PAZ-1 that contains a DMS core along with phenyl units, and thus, the lowest carbon content in the series. From DSC analysis, the substitution of phenyl groups in PAZ-1/3 by biphenyl moieties in PAZ-2/4 allowed to obtain oligo(azine)s with lower T-g values. PAZ-4 showed a UV-A absorption with optical band-gap values of 2.91 and 2.65 eV from UV-vis (solution) and DRS (films), respectively. PL analysis showed a violet emission. PAZ-4 showed resistivity of 29.24 omega cm, similar to wide-band gap materials. Their contact angle measurements showed a critical surface tension of 42.29 dynes/cm, revealing its hydrophobicity. AFM analysis indicated that the PAZ-4 films had homogeneous surfaces. Young's modulus close to 4.46 GPa was established by microindentation for the PAZ-4 thin-films.

著录项

获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号