首页> 外文期刊>Journal of Applied Polymer Science >Study of failure behaviors of rigid polyurethane foam treated under thermal and vibration conditions by experiment and numerical simulation
【24h】

Study of failure behaviors of rigid polyurethane foam treated under thermal and vibration conditions by experiment and numerical simulation

机译：Study of failure behaviors of rigid polyurethane foam treated under thermal and vibration conditions by experiment and numerical simulation

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相关主题

摘要

Failure mechanism of rigid polyurethane foam (RPUF) treated under different conditions was studied by means of experiments and numerical simulation. Thermal degradation mechanism of RPUF under different temperatures was characterized by thermogravimetric analysis-Fourier transform infrared spectrometry coupled with gas chromatography-mass spectrometry (TG-FTIR-GC-MS) in air and nitrogen atmosphere, respectively. And the vibration failure mechanism of RPUF was analyzed by finite element analysis (FEA) and extended finite element method (XFEM). The experimental results indicated that the failure mode in nitrogen was the broken of carbamate groups, and in air was the broken of carbamate groups and the radical decomposition of ether groups. Numerical simulation suggested that there was vibration stress concentration in the center of foam prism, which was easy to produce sliding and opening fatigue cracks during random vibration.

著录项

获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号