Synergized bioperformance bone scaffolds of poly(vinyl alcohol)/silk fibroin particles with TiO2 as the base bone-mimicking materials for oral and maxillofacial surgery

机译：Synergized bioperformance bone scaffolds of poly(vinyl alcohol)/silk fibroin particles with TiO2 as the base bone-mimicking materials for oral and maxillofacial surgery

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相关主题

摘要

Scaffolds of poly(vinyl alcohol) (PVA)/silkfibroin particles (SP) with TiO2 particles were prepared as the bone-mimicking materials. PVA solutions were mixed with SP in the ratio 2:1 (w/w), loaded with TiO2 particles at 0, 0.8, 1.6, and 3.2% (w/w) before freeze-thawing for 10 cycles and then freeze-dried. Molecular organization and morphology were characterized and observed by Fourier transform infrared spectroscopy and scanning electron microscopy. Tests included contact angle, swelling, mechanical behaviors, and cell viability and proliferation, alkaline phosphatase (ALP) activity, calcium deposition, and protein synthesis that showed molecular interactions of the PVA, SP, and TiO2. Scaffolds with TiO2 had higher Young's modulus, stress at maximum load, and contact angle, but had lower swelling, smaller pore size, lower porosity, and greater homogenous size distribution than without TiO2. TiO2 at 1.6% (w/w) had the most homogeneous pore distribution with interconnected porosity supporting cell viability and proliferation, ALP activity, calcium deposition, and protein synthesis as well as synergized bioperformance.

著录项

获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号