首页> 外文期刊>Journal of Applied Polymer Science >Thermal behavior evaluation of benzoxazine reinforced with macadamiabiomass composites
【24h】

Thermal behavior evaluation of benzoxazine reinforced with macadamiabiomass composites

机译：Thermal behavior evaluation of benzoxazine reinforced with macadamiabiomass composites

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相关主题

摘要

Recently, to improve the properties, reduce the amount of polymeric materials, the time of disposal in landfills and the cost of composite parts, the incorporation of vegetal biomass was considered. In this study, composites with 10 and 20 v/v of benzoxazine resins and macadamia nutshell (50#) were made via hand layup with in natura biomass and hydrothermally treated (121 degrees C/45 min in an autoclave). Thermogravimetry indicates that the initial temperature of biomass degradation (209 degrees C) allows it to be used with the resin (oven curing at 190 degrees C). The enthalpies obtained from the DSC indicate that the percentage of cure increased with the biomass. FT-IR tests indicate that the hydrothermal treatment collapsed part of the lignin and extracted lignocellulosic material. There was no significant modification of the glass transition temperature obtained in DMA and TMA with the introduction of biomass. Optical microscopy showed that the treated reinforcement showed a greater variation in size forming lumps. Based on these results, these composites can be used in the replacement of synthetic composites, contributing to a decrease in the consumption of petroleum derivatives and with this, reducing the disposal in landfills and dumps.

著录项

获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号