首页> 外文期刊>Journal of Applied Polymer Science >Preparation of poly(melamine-formaldehyde-2,2 '-bis (trifluoromethyl)benzidine) high-performance fibers
【24h】

Preparation of poly(melamine-formaldehyde-2,2 '-bis (trifluoromethyl)benzidine) high-performance fibers

机译：Preparation of poly(melamine-formaldehyde-2,2 '-bis (trifluoromethyl)benzidine) high-performance fibers

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相关主题

摘要

Melamine formaldehyde fiber is widely used in various fields because of its excellent heat resistance and flame-retardant properties. In this study, melamine and paraformaldehyde are used as the main raw materials, 2,2'-bis (trifluoromethyl)benzidine (TFMB) is successfully introduced into the molecular chain. The TFMB modified spinning solutions (MF-TFMB) are obtained by one-step copolymerization, the TFMB-modified melamine-formaldehyde fibers (MFF-TFMB) are prepared by city spinning. The surface contact angle and surface energy are measured by a contact angle measuring instrument. The thermal stability and mechanical properties of the fibers are measured by a thermogravimetric analyzer and a single-fiber strength tester. The results show that the introduction of the TFMB group reduces the surface free energy of the polymer and effectively improves the heat resistance and mechanical properties of the fiber. When the addition amount of TFMB is 3, the MFF-TFMB-3 fiber has smooth surface and bubble-free inside, the breaking strength is 2.25 cN/dtex and the elongation at break is 11.85. The limiting oxygen index is 32.5, and the mass loss rate is decreased from 63.88 to 51.36 at 400 degrees C. The fiber has excellent thermal stability and flame-retardant properties.

著录项

获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号