首页> 外文期刊>Journal of thermal analysis and calorimetry >Thermal behavior of PLA plasticized by commercial and cardanol-derived plasticizers and the effect on the mechanical properties
【24h】

Thermal behavior of PLA plasticized by commercial and cardanol-derived plasticizers and the effect on the mechanical properties

机译：Thermal behavior of PLA plasticized by commercial and cardanol-derived plasticizers and the effect on the mechanical properties

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相关主题

摘要

This paper is aimed at studying the thermal properties of poly(lactic acid), PLA with different plasticizers. Plasticized PLA was obtained by mixing and extruding PLA with 20 mass of neat cardanol, epoxidized cardanol acetate (ECA) and poly(ethylene glycol) (PEG) 400. The glass transition of completely amorphous samples, melting and crystallization behavior of plasticized PLA were analyzed by differential scanning calorimetry. Results obtained show that, below T-g, a higher enthalpy relaxation occurs for PLA plasticized by cardanol derivatives. This is indicative of a faster mobility of PLA chains below T-g, when cardanol derivatives are used as plasticizers. On the other hand, an opposite behavior was observed for the crystallization studies. In facts, a much faster crystallization was found for PLA plasticized by PEG, which in turn indicates a much higher mobility of PLA chains above T-g compared to PLA plasticized by cardanol derivatives. Mechanical properties obtained on completely amorphous samples show that PLA plasticized by ECA is characterized by lower modulus, which is indicative of a more efficient plasticization. On the other hand, the thicker crystals formed during crystallization of PLA plasticized by ECA involve a more relevant increase in the modulus in semicrystalline samples.

著录项

获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号