Fatigue Behavior of High-Performance Steel Beams Subjected to Different Corrosion Conditions

机译：Fatigue Behavior of High-Performance Steel Beams Subjected to Different Corrosion Conditions

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相关主题

摘要

Abstract The existing research mainly considers the fatigue properties of steel structures under the influence of the environment, corrosion rate, and load conditions without considering the effect of corrosion locations and areas. However, corrosion can happen to a steel structure in a practical engineering setting at any position. This paper investigates the fatigue behavior of high-performance steel beams (Q550E) subjected to different corrosion conditions through various tests. Results show that the fatigue life of the wholly corroded steel beams decreases as the frequency increases and increases as the stress ratio increases. Additionally, local corrosion has a greater impact on flexural stiffness than whole corrosion, and the lower half area has a greater impact than the right half area. Other corroded steel beams, with the exception of SCU-10, have fracture positions that are within the corrosion area. Because, despite the corrosion in the bending shear section, the fatigue strength of the corrosion area is higher than that of the fracture location. In addition, the degradation curves of the mid-span flexural stiffness of other steel beams under cyclic loading have not observed S-shaped curve characteristics, with the exception of GC-10B and SCU-20.

著录项

获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号