Structure-property relationship in film and blow molding type high-density polyethylene polymers from a slurry-process industrial plant

机译：Structure-property relationship in film and blow molding type high-density polyethylene polymers from a slurry-process industrial plant

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相关主题

摘要

In this study, the microstructural, flow, and mechanical properties of two commercially available high-density polyethylene (HDPE) samples with different particle sizes were quantified. Specifically, two different blow molding and film grade HDPEs produced by the same catalyst under different conditions were acquired in powder form after dryer section of an industrial plant. They were fractioned according to their particle sizes into six samples: = 500 mu m. According to sieve analysis, the film grade (D-50 = 304 mu m) had larger particle sizes related to the counterpart injection sample (D-50 = 289 mu m). A peak value in density, bulk density, viscosity molecular weight (M-v), melt flow index (MFI), and comonomer content characteristics was found in the particles with the diameter of 125-200 mu m in both samples, indicating extremely non-homogeneity of these HDPE samples. Chemical composition distribution (CCD) of the as received polymers as well as sieved fractions was surveyed via SSA or TREF analyses. The film sample represented lower MFI and density and higher M-v and comonomer content in all fractions, originated from different reactor conditions during the samples synthesis, which translate into improved mechanical properties comparing with the blow molding sample.

著录项

获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号