首页> 外文期刊>Journal of thermal analysis and calorimetry >The effect of cobalt addition on sintering and microstructural behaviour of silver-tungsten (Ag-W) composite
【24h】

The effect of cobalt addition on sintering and microstructural behaviour of silver-tungsten (Ag-W) composite

机译：The effect of cobalt addition on sintering and microstructural behaviour of silver-tungsten (Ag-W) composite

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相关主题

摘要

The present investigation has been revealed that homogeneous silver-tungsten (Ag-W) composite powders doped with cobalt as sinter aid can be produced by the twostage reduction of co-precipitated tungstate. The sintering of the powders has been studied using dilatometry and the results showed that the critical level for activated sintering is of the order of 0.3 mass percent cobalt with respect to the tungsten content of the compact powder. This critical level is equivalent to approximately six to seven atomic layer coverage of the tungsten particles by cobalt. The levels of cobalt addition above the critical amount leads to the formation of cobalt tungsten (CoW_3) intermetallic compound precipitates, which become trapped within the silver phase in the sintered composite material. Microstructural evaluation of sintered specimens has been carried out using optical and electron microscopy. Transmission electron microscopy results revealed the neck formation between adjacent tungsten particles along with the presence of silver around the tungsten particles. Energy dispersive X-ray (EDX) analysis also confirmed that amounts of cobalt was 0.3 mass percent, in the region containing the silver at the tungsten particle interface which agreed with the level of activated sintering.

著录项

获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号