首页> 外文期刊>Macromolecular Research >Fabrication of a Strong Artificial Nacre Based on Tannic Acid-Functionalized Graphene Oxide and Poly(vinyl alcohol) Through Their Multidentate Hydrogen Bonding
【24h】

Fabrication of a Strong Artificial Nacre Based on Tannic Acid-Functionalized Graphene Oxide and Poly(vinyl alcohol) Through Their Multidentate Hydrogen Bonding

机译：Fabrication of a Strong Artificial Nacre Based on Tannic Acid-Functionalized Graphene Oxide and Poly(vinyl alcohol) Through Their Multidentate Hydrogen Bonding

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相关主题

摘要

A strong graphene oxide (GO)-based artificial nacre is developed by using a simple and efficient interfacial chemistry. GO is simultaneously reduced and functionalized with tannic acid (TA) and the resulting TA-reduced GO (TA-RGO) exhibits a high aqueous dispersibility owing to abundant phenol groups. TA-RGO sheets are incorporated with poly(vinyl alcohol) (PVA) and then assembled into an artificial nacre-like structure by vacuum-assisted filtration to induce the formation of multidentate interfacial hydrogen bonding between TA-RGO and PVA. Based on the multidentate hydrogen bonding, the resulting TA-RGO/PVA (1 wt) composite film presented an overall and efficient reinforcement of tensile strength (186.1 +/- 12.8 MPa), modulus (15.2 +/- 1.2 GPa) and toughness (1546 +/- 248 kJ/m(3)) compared to those of GO (83.3 +/- 5.4 MPa, 8.9 +/- 0.4 GPa and 1434 +/- 152 kJ/m(3)) and TA-RGO (87.6 +/- 10.6 MPa, 13.8 +/- 1.4 GPa and 306 +/- 51 kJ/m(3)), respectively. The present study demonstrates the rational design of interfacial interaction can greatly improve the performance of a structural composite material.

著录项

获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号