首页> 外文期刊>Journal of Applied Polymer Science >Preparation of a novel phosphorus-nitrogen flame retardant and its effects on the flame retardancy and physical properties of polyketone
【24h】

Preparation of a novel phosphorus-nitrogen flame retardant and its effects on the flame retardancy and physical properties of polyketone

机译：Preparation of a novel phosphorus-nitrogen flame retardant and its effects on the flame retardancy and physical properties of polyketone

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相关主题

摘要

In this study, a novel phosphorus-nitrogen flame retardant (PNFR) was synthesized, and its flame retardancy for polyketone (PK) was systematically investigated. The chemical structure of PNFR was characterized using NMR spectroscopy. The PNFR was considered to generate phosphoric acid, which catalyzed the char formation reaction of PK via condensed-phase decomposition. When 7 wt PNFR was incorporated into PK, the limiting oxygen index value was increased from 20.2 to 25.9. In addition, this PK-PNFR sample achieved the rating of VTM-0 because it exhibited self-extinguishable properties and did not drip when fire was removed from it. As the PNFR content increased, while the initial decomposition temperature decreased, the amount of residual char considerably increased. Thus, the PNFR was thought to impart flame-retarding ability to PK via superior condensed-phase mechanism. Additionally, the decrease in melting temperature and enthalpy of fusion was observed after the addition of PNFR, which implied that the PNFR could act as plasticizer for PK.

著录项

获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号