首页> 外文期刊>Journal of Applied Polymer Science >Improved thermal conductivity of epoxy resins using silane coupling agent-modified expanded graphite
【24h】

Improved thermal conductivity of epoxy resins using silane coupling agent-modified expanded graphite

机译：Improved thermal conductivity of epoxy resins using silane coupling agent-modified expanded graphite

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相关主题

摘要

A silane coupling agent was used to modify the surface of expanded graphite (EG), which was subsequently used as a thermally conductive filler to fabricate diglycidylether of bisphenol-A (DGEBA)/EG composites with high thermal conductivity via hot blending and compression-curing processes. The surface characteristics of silane coupling agent-modified EG (Si@EG) were characterized by a variety of analytical techniques. The effects of the Si@EG content on the thermal conductivity, thermal stability, impact strength, and morphology of the DGEBA/Si@EG composites were investigated. The results revealed that the addition of 80 wt. Si@EG increased the thermal conductivity of the composites from 0.17 to 10.56 W/m K, which was 61.1 times higher than that of pristine DGEBA. The initial decomposition temperature of the composite containing 80 wt. Si@EG was 60.6? higher than that of pristine DGEBA. The impact strength of the composites decreased from 2.0 to 0.87 kJ/m(2) when the Si@EG content increased from 0 to 80 wt.. The scanning electron microscopy images of the fractured surfaces revealed that the EG sheets in the DGEBA matrix formed a continuous thermally conductive path at high Si@EG contents.

著录项

获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号