首页> 外文期刊>Journal of Applied Polymer Science >Broadband microwave absorbing materials for green electronics based on poly (lactic acid)/ethylene-vinyl acetate copolymer blends loaded with carbon nanotube
【24h】

Broadband microwave absorbing materials for green electronics based on poly (lactic acid)/ethylene-vinyl acetate copolymer blends loaded with carbon nanotube

机译：Broadband microwave absorbing materials for green electronics based on poly (lactic acid)/ethylene-vinyl acetate copolymer blends loaded with carbon nanotube

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相关主题

摘要

Partially bio-based conducting polymer nanocomposites constituted by poly(lactic acid) (PLA)/ethylene-co-vinyl acetate (EVA) (50:50 wt) blend loaded with different amounts of carbon nanotube (CNT) were prepared for developing microwave absorbing materials. The effect of EVA characteristics and the mixing conditions on the electrical conductivity was investigated. The higher conductivity value was achieved using PLA@CNT master batch and EVA with 28 of VA. In fact, this system presented electrical percolation threshold of 7 x 10(-4) volume fraction and a conductivity value of 3 x 10(-3) S/m with the addition of 0.9 wt (0.58 vol) of CNT. A minimum reflection loss of -29 dB (electromagnetic (EM) attenuation of around 99.9) at 11.7 GHz and the bandwidth (<-10 dB) of 4.9 GHz was observed with the presence of 0.58 vol of CNT, whereas RL value of around -39.4 dB (EM attenuation of around 99.99) at 14.7 GHz and a bandwidth of 4.6 GHz was observed for the composite loaded with 0.25 vol of CNT. Due to the outstanding microwave absorption properties and wide absorption bandwidth with low amount of CNT, these composites are promising candidates for flexible materials suitable for shielding electronic devices in a wide frequency range.

著录项

获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号