首页> 外文期刊>Journal of Materials Research >Effect of ball milling time on the magnetoelectric coupling effect of the multiferroic liquid CoFe2O4-Ba0.8Sr0.2TiO3
【24h】

Effect of ball milling time on the magnetoelectric coupling effect of the multiferroic liquid CoFe2O4-Ba0.8Sr0.2TiO3

机译：Effect of ball milling time on the magnetoelectric coupling effect of the multiferroic liquid CoFe2O4-Ba0.8Sr0.2TiO3

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相关主题

摘要

In this thesis, CoFe2O4 (CFO) and Ba0.8Sr0.2TiO3 (BST) particles were prepared by chemical co-precipitation and sol-gel methods, respectively. On this basis, the particles were surface modified and then the CFO-BST composite liquid was prepared by adding CFO: BST = 1:1 to the insulating base solution. XRD results showed that pure phase CFO and BST particles were successfully prepared. The maximum dielectric constant and residual polarization intensity were obtained at low frequency (200 Hz) at 30 h. However, the relative rates of change of dielectric constant and ferroelectricity under the action of magnetic field were increasing and then decreasing. At 2 h, the maximum rate of change of magnetic dielectric response (3.15) and the maximum rate of change of magnetoelectric response (256.4) were obtained, meanwhile, a coupling coefficient of 8.34 V/(cm Oe) was obtained. This value is several orders of magnitude greater than that of conventional ceramics and promises new applications.

著录项

获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号