首页> 外文期刊>Journal of Applied Polymer Science >Increased reliability of modified polyolefin backsheet over commonly used polyester backsheets for crystalline PV modules
【24h】

Increased reliability of modified polyolefin backsheet over commonly used polyester backsheets for crystalline PV modules

机译：Increased reliability of modified polyolefin backsheet over commonly used polyester backsheets for crystalline PV modules

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相关主题

摘要

The weathering stability of polymeric backsheets is very important for the reliability of photovoltaic (PV) modules. In addition to reliability, cost reduction and sustainability are upcoming challenges the PV backsheet industry is facing with. The most commonly used material for PV backsheets is poly(ethylene-terephthalate)-PET. However, PET is in general very sensitive to hydrolysis, which leads to chain scission and causes embrittlement, cracking, delamination, and dimensional instability of the backsheet. Compared to that newly developed modified polyolefin backsheets have favorable selective permeation properties and high mechanical flexibility, which could be key properties for backsheets in terms of higher PV module reliability. In this work, the weathering stability of PET/fluoropolymer backsheet and an alternative coextruded polyolefin-backsheet was investigated in terms of thermal and mechanical stability. Both materials were artificially aged and the changes caused by aging were investigated. The polyester-based backsheet showed embrittlement and reduced elongation at break for 70. The polyolefin-based backsheet retained its mechanical flexibility even after 2000 h of aging under damp-heat conditions, with no significant physical or chemical aging processes occurring. The comparison of the results of both backsheets suggests that the polyolefin backsheet is a promising candidate for the reduction of cracks and delamination in the field. (c) 2020 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2020, 137, 48899.

著录项

获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号