首页> 外文期刊>Journal of Applied Polymer Science >Interdiffusion during film formation of ionically cross-linked acrylics investigated with Forster resonance energy transfer (FRET)
【24h】

Interdiffusion during film formation of ionically cross-linked acrylics investigated with Forster resonance energy transfer (FRET)

机译：Interdiffusion during film formation of ionically cross-linked acrylics investigated with Forster resonance energy transfer (FRET)

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相关主题

摘要

Polymer interdiffusion is crucial to obtain continuous films from aqueous polymer dispersions. Here, interdiffusion in films from dispersions of acrylates which were ionically cross-linked prior to film formation was studied by Forster resonance energy transfer analysis. Dispersions of copolymers of n-butyl acrylate, methacrylic acid, and zinc dimethacrylate (ZnDMA) were investigated. ZnDMA was used as a co-monomer to ionically cross link the polymers during the synthesis. Ionic cross-linking does not prevent interdiffusion even at high gel contents. Interdiffusion data were compared with results of tensile tests on final films. Films of ionically cross-linked polymers fracture at both higher stress and strain than films of covalently cross-linked polymers. Further interdiffusion studies addressed effects of temperature and humidity. Both increased temperature and humidity accelerate interdiffusion of ionically cross-linked polymers. Thus, using ZnDMA allows for preparing dispersions which can form continuous films. Also, no volatile organic compounds are released during the film formation. (c) 2020 The Authors. Journal of Applied Polymer Science published by Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2020, 137, 48972.

著录项

获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号