首页> 外文期刊>Polymers for advanced technologies >Grafting alkynyl groups on the surface of nano‐aramid fibers towards flame retardant thermoplastic polyurethane
【24h】

Grafting alkynyl groups on the surface of nano‐aramid fibers towards flame retardant thermoplastic polyurethane

机译：Grafting alkynyl groups on the surface of nano‐aramid fibers towards flame retardant thermoplastic polyurethane

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相关主题

摘要

In this work, para‐aramid fibers were dispersed into para‐aramid nanofibers (ANF) by deprotonation process, and then modified by 3‐chloropropyne (PC) via covalent bonding interaction. The resultant nanofiber (ANF‐PC) as a flame retardant was blended with thermoplastic polyurethane (TPU) to obtain fire‐retardant TPU nanocomposites. The addition of 0.250 wt ANF‐PC reduced the peak heat release rate, total heat release, total smoke release, and peak CO release rate of TPU by 47.7, 31.5, 16.4, and 45.1, respectively. The char yield of TPU/ANF‐PC0.250 was increased from 7.7 (TPU/ANF0.250) to 13.7. The flame‐retardant effect of ANF‐PC in TPU composites can be attributed to its carbonization effect in the condensed phase, which increased the char yields and graphitization degree of char residue. In addition, the presence of ANF‐PC increased the tensile strength and breaking strain of TPU by 645 and 578 compared to untreated ANF, due to the improved dispersion state of ANF‐PC.

著录项

获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号