首页> 外文期刊>iucrj >Detection and characterization of folded-chain clusters in the structured melt of isotactic polypropyl­ene
【24h】

Detection and characterization of folded-chain clusters in the structured melt of isotactic polypropyl­ene

机译：Detection and characterization of folded-chain clusters in the structured melt of isotactic polypropyl­ene

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相关主题

摘要

Despite ceaseless efforts in past decades, the memory effect of semi-crystalline polymers has not been elucidated completely yet. An important reason why is that residual lamellar crystals in the structured melt are difficult to characterize. Recently, we developed a new small-angle X-ray scattering (SAXS) theory Li et al. (2019). IUCrJ, 6, 968–983 and Fourier transform method Li et al. (2020). CrystEngComm, 22, 3042–3058 for lamellar crystals that could derive structural information from SAXS readily. In this study, we tried to employ the new theory and method to characterize residual lamellar crystals in the structured melt. It was found that although scattering peaks cannot be observed in raw scattering profiles, they actually exist. Subtracting free-melt scattering and multiplying by q4 benefit the observation of these weak scattering peaks. With the new Fourier transform method, it was found that indeed as proposed previously, thicker lamellar crystals exist in the structured melt. To determine the lateral size of residual lamellar crystal especially, a new method was developed under the guidance of the new theory. With the new method, it was found that although the crystallinity is very low (∼1 at 174°C), the lateral sizes in the structured melts are still large, e.g. 45.3 nm at 174°C, much greater than the critical nucleation size. This implies that these residual lamellar crystals can act as athermal nuclei after quenching to a lower temperature, as proposed by Ziabicki Alfonso (1994). Colloid Polym. Sci. 272, 1027–1042; (2002). Macromol. Symp. 185, 211–231 more than 20 years ago. The methodologies proposed here could also be applied to other polymer lamellar systems.

著录项

获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号