首页> 外文期刊>Journal of Applied Polymer Science >Mechanical properties of 3D printed micro-nano rice husk/polylactic acid filaments
【24h】

Mechanical properties of 3D printed micro-nano rice husk/polylactic acid filaments

机译：Mechanical properties of 3D printed micro-nano rice husk/polylactic acid filaments

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相关主题

摘要

In this study, micro-nano rice husks (MNRH) fibers are compounded in polylactic acid (PLA) to produce 3D-printed filaments by using melt blending method, and some properties of the printed samples of different surface treatment processes are measured. Two silane coupling agents of KH550 and KH570 are severally used on MNRH and PLA to mitigate the surface quality deficiencies for an intimate interfacial bond. Microstructural analysis shows that the MNRH fibers of the composites treated by silane coupling agent have a better dispersing performance. Fourier transform infrared illustrates that the KH550 and KH570 are successfully grafted onto PLA and MNRH fibers. Thermogravimetric analysis (TGA/DSC) suggests that the thermostability and crystallinity of the composites treated by silane coupling agents are enhanced. Water absorption experiments shows that the water resistance of the composites is greatly increased by KH550 and KH570. In comparison with pure PLA, the tensile strength, tensile modulus, bending strength and bending modulus of the 6 wt. MNRH/PLA composites that treated by KH550 and KH570 are enhanced by 83, 98, 54, and 61, respectively. The composites treated by KH550 and KH570 demonstrates the best performance, suggesting that they have great potential for use as an environmentally friendly alternative material in automotive interiors.

著录项

获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号