首页> 外文期刊>Materials Science and Technology: MST: A publication of the Institute of Metals >Characterisation of tensile deformation behaviour of Fe-25Cr-35Ni-based alloy at high temperature
【24h】

Characterisation of tensile deformation behaviour of Fe-25Cr-35Ni-based alloy at high temperature

机译：Characterisation of tensile deformation behaviour of Fe-25Cr-35Ni-based alloy at high temperature

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相关主题

摘要

Fe-25Cr-35Ni-based alloy tensile deformation behaviour was studied through tensile test at strain rates of 5 x 10(-4), 10(-3), 5 x 10(-3) and 10(-2) s(-1) from 900 to 1023 degrees C in this paper. The flow stress has a good correlation with testing temperature and strain rate. TEM and SEM were used to analyse the microstructure evolution. The results show that DRV and DRX are the important factors for reducing the flow stress during hot tensile deformation. The occurrence of DRV and DRX was confirmed by TEM micrographs in high temperature tensile deformation. The hyperbolic sine-type equation with deformation activation energy and temperature describes Fe-25Cr-35Ni-based alloy hot tensile deformation, and the deformation activation energy is 5.24 x 10(2) kJ mol(-1).

著录项

获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号