首页> 外文期刊>Fire and materials >Evaluating the use of calcium hydrogen phosphate dihydrate as a mineral-based fire retardant for application in melamine-urea-formaldehyde (MUF)-bonded wood-based composite materials
【24h】

Evaluating the use of calcium hydrogen phosphate dihydrate as a mineral-based fire retardant for application in melamine-urea-formaldehyde (MUF)-bonded wood-based composite materials

机译：Evaluating the use of calcium hydrogen phosphate dihydrate as a mineral-based fire retardant for application in melamine-urea-formaldehyde (MUF)-bonded wood-based composite materials

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相关主题

摘要

Calcium hydrogen phosphate dihydrate (DCPD) was evaluated for its potential as a mineral fire retardant (FR) for application in melamine-urea-formaldehyde (MUF)-bonded wood composites. The efficacy as FR was studied in melamine-urea-formaldehyde (MUF)-bonded three-layer particleboard as a function of addition quantities of 10-, 20- and 30 wt. Resistance to fire and mechanical properties were determined by measuring the self-extinguishing time after flame exposure and internal bond strength, respectively. Combustion behavior was examined on samples with 20 wt DCPD addition by performing cone calorimetry experiments. The efficacy of DCPD was evaluated by determining the heat release, total heat release rate, smoke production, and smoke production rate and compared to another promising mineral-based fire-retardant composition (FRC) based on hydroxyapatite (HA) with deliquescent salt and HA alone. The effect of FR on the curing behavior of MUF in relation to mechanical properties was determined through viscosity measurements of MUF with 10 wt addition of FR. The results confirmed the fire-retardant characteristics of DCPD in wood composites, albeit at higher application rates when compared to the FRC, however with no negative impact on resin curing time or mechanical strength. Based on the demonstrated compatibility in MUF, DCPD is considered a promising mineral extender of other FRs for application in UF-based wood composites.

著录项

获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号