首页> 外文期刊>Journal of Applied Polymer Science >Preparation and evaluation of acryloyl morpholine modified emulsion fracturing fluid thickener with high temperature resistance and salt resistance
【24h】

Preparation and evaluation of acryloyl morpholine modified emulsion fracturing fluid thickener with high temperature resistance and salt resistance

机译：Preparation and evaluation of acryloyl morpholine modified emulsion fracturing fluid thickener with high temperature resistance and salt resistance

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相关主题

摘要

To prepare the thickener of fracturing fluid with temperature resistance, salt resistance and quick dissolution, an emulsion thickener (ASC) was synthesized by acrylamide, acrylic acid, 2-acrylamide-2-methylpropanesulfonic acid, and acryloyl morpholine. The dissolution, salt resistance and drag reduction of ASC, and the viscoelasticity, temperature resistance and shear resistance and gel breaking properties of fracturing fluid formed by ASC and zirconium crosslinker were investigated. The results showed that the sticky time of ASC was less than 60 s and the drag reduction rate was 72.5 in 100,000 mg/L brine, showing that ASC had thickening ability in high salinity brine and satisfied the requirements of continuous fluid preparation on the fracturing process. The viscosity of ASC fracturing fluid was 98 mPa s after shearing at 200 ? and 170 s(-1) for 150 min when the salinity was 100,000 mg/L. When the ammonium persulfate concentration was 400 mg/L, the viscosity of the broken fluid was 4.0 mPa s. The temperature resistance, salt resistance and shear resistance of ASC emulsion fracturing fluid could be significantly improved by the introduction of acryloyl morpholine, ASC fracturing fluid had the characteristics of high elasticity and low viscosity, which could meet the application requirements under ultra-high temperature reservoirs.

著录项

获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号