abstract_textpHerein, the influence of adding titania to the carbonaceous alumina coating of Al2O3-C filters on the interactions with molten steel is investigated. Therefore, coated filters are immersed for 30 s in molten steel (42CrMo4) at 1580 degrees C. Mainly by microstructural and chemical analyses, the immersed filters as well as the solidified steel are characterized. Due to the reducing atmosphere of the heat treatment during sample manufacturing, the formation of aluminum titanate phases in the coating is not observed. During immersion, on the one hand, titania acts as the sintering agent for alumina within the coating and for precipitated alumina inclusions from the melt. On the other hand, dissolved titanium in the melt decreases the surface tension and thus increases wetting of the steel melt on the filter surface. The results indicate that more but smaller alumina inclusions remain in the solidified steel if titania is added to the coating. Thus, the modification of alumina inclusions by adding titania to the filter coating presents a way to tailor these inclusions depending on the product's application./p/abstract_text

著录项

获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号