首页> 外文期刊>Journal of Applied Polymer Science >Preparation of poly(lactic acid) with excellent comprehensive properties via simple deformation or microfibrillation of spherulites
【24h】

Preparation of poly(lactic acid) with excellent comprehensive properties via simple deformation or microfibrillation of spherulites

机译：Preparation of poly(lactic acid) with excellent comprehensive properties via simple deformation or microfibrillation of spherulites

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相关主题

摘要

Abstract Our work overcomes the long‐standing challenge to achieve comprehensive improvements in thermo/mechanical properties of poly(lactic acid) (PLA), especially for impact toughness, strength, ductility, stiffness, and heat resistance. Simple deformation or microfibrillation of spherulites can create excellent thermo/mechanical properties making PLA compete against conventional petrochemical‐based polymers. It was performed by pressure‐induced‐flow (PIF) processing, and produced typical deformed spherulite structure and brick‐mud structure. It was found that the critical deformation degree of spherulites was around 2.7, beyond which spherulites would fragment. Through three transition stages of spherulite structures, deformed spherulite structures, and brick‐mud structure, PLA exhibited an enhancement of orientation, storage modulus and glass transition temperature. And a substantial increase was proved in impact strength (105.6 kJ/m2), tensile strength (148.4 MPa) and elongation at break (107.7), which can be comparable to most engineering plastics. Both the deformed spherulite structures and the brick‐mud structures can enhance the impact toughness of PLA by increasing the fracture path of cracks. Besides, the evolution of the microstructure for a sandwich structure during PIF‐processing was proposed.

著录项

获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号