Self-healing of matrix cracking and delamination damage assessment in microcapsules reinforced carbon fibre epoxy composite under flexural loading

Pittala Raj Kumar; Dhanaraju Goteti; Ben B. SatishBen Avinash

首页> 外文期刊>Composite structures >Self-healing of matrix cracking and delamination damage assessment in microcapsules reinforced carbon fibre epoxy composite under flexural loading

【24h】

Self-healing of matrix cracking and delamination damage assessment in microcapsules reinforced carbon fibre epoxy composite under flexural loading

机译：Self-healing of matrix cracking and delamination damage assessment in microcapsules reinforced carbon fibre epoxy composite under flexural loading

获取原文

获取原文并翻译 | 示例

掌桥外文数据库（机构版） >>

开具论文收录证明 >>

文献代查 >>

页面导航

摘要
著录项
相关主题

摘要

Structural integrity of micro cracked CFRP composite structures can be re-established by incorporating the microcapsules based self-healing system into the composite. In the current study, in order to fabricate capsules reinforced CFRP composite, 0.54: 0.39: 0.07 vol fractions of matrix, carbon fibre and separately encapsulated epoxy, hardener microcapsules were employed. Effect of microcapsules addition and induced damage on the flexural strength of the composite were investigated. It was noticed that flexural strength decreases with the increase in capsules concentration and for 5 wt capsules reinforced composite flexural strength reduced by 21.73, 29.32 due to induce of matrix cracking and delamination damage respectively. In order to assess self healing performance of the composite, different damage events were induced in the composite and healing efficiency was evaluated based on the recovery in flexural strength. Effect of capsules wt, healing temperature and pressure on the healing efficiency were assessed and noticed higher healing efficiencies at elevated temperature and pressure healing conditions. Healing efficiencies of 71.30, 54.21 were obtained at optimal healing conditions for matrix cracking, delamination damage recovery respectively. Crack path deflection, crack pinning and capsules rupture mechanisms were observed in the microstructural investigation of fracture surface of capsule reinforced composite.

著录项

来源
《Composite structures》 |2022年第7期|115691.1-115691.13|共13页
作者
Pittala Raj Kumar; Dhanaraju Goteti; Ben B. SatishBen Avinash;
展开▼
作者单位

Natl Inst Technol, Dept Mech Engn, Warangal 506004, Telangana, India|Koneru Lakshmaiah Educ Fdn, Dept Mech Engn, Vaddeswaram 522502, Andhra Pradesh, India;

Natl Inst Technol, Dept Mech Engn, Warangal 506004, Telangana, India;

Avanthi Inst Engn & Technol, Dept Mech Engn, Visakhapatnam 531113, Andhra Pradesh, India;

展开▼
收录信息美国《科学引文索引》(SCI);美国《工程索引》(EI);
原文格式 PDF
正文语种英语
中图分类
关键词
Self-healing; Smart materials; Flexural properties; Microcapsules; Carbon fibre epoxy composite;

Self-healing of matrix cracking and delamination damage assessment in microcapsules reinforced carbon fibre epoxy composite under flexural loading