首页> 外文期刊>Journal of environmental sciences >Highly active mixed-phase TiO{sub}2 photocatalysts fabricated at low temperature and the correlation between phase composition and photocatalytic activity
【24h】

Highly active mixed-phase TiO{sub}2 photocatalysts fabricated at low temperature and the correlation between phase composition and photocatalytic activity

机译：Highly active mixed-phase TiO{sub}2 photocatalysts fabricated at low temperature and the correlation between phase composition and photocatalytic activity

获取原文
获取原文并翻译 | 示例
   

获取外文期刊封面封底 >>

       
页面导航
  • 摘要
  • 著录项
  • 相关主题

摘要

The idea of varying volume ratio of water to ethanol in solvent was firstly employed to yield phase composition controllable mixed-phase titanium dioxide (TiO{sub}2) photocatalysts via a low temperature solvothermal route at 353 K. It was found that anatase contents increase from 0 to 100 with increase of ethanol contents in solvent. The mixed-phase TiO{sub}2 with 60 anatase content exhibited the best photocatalytic activity in photodecomposing formaldehyde (FAD) under UV light irradiation, which increases by about 270 or 400 in comparison with single rutile or anatase TiO{sub}2, and is slightly better than commercial mixed-phase TiO{sub}2 (P25). The synergistic effect in mixed-phase TiO{sub}2 including antenna effect by rutile phase and the activation effect by anatase phase was observed. Further, partially quantitive correlation between phase composition and photocatalytic activity was ascribed to maximizing the synergistic effect and an optimal value of anatase content about 60 in mixed-phase TiO{sub}2 photocatalyst was therefore suggested.