首页> 外文期刊>journal of applied polymer science >Novolac epoxy resins and positron annihilation
【24h】

Novolac epoxy resins and positron annihilation

机译：Novolac epoxy resins and positron annihilation

获取原文
           
页面导航
  • 摘要
  • 著录项
  • 相关主题

摘要

AbstractFour kinds of epoxy resins: cresol novolac, tris‐hydroxyphenylmethane, tetramethylbiphenol, and bisphenol A, were cured with phenol novolac epoxy resins. Characteristics of these epoxy compounds were studied by the positron annihilation lifetime (PAL) technique. Glass transition temperatures, thermal expansion coefficients, and volume of intermolecularspace holes among polymer chains were obtained from the lifetime, τ3, of the long‐lived component ofortho‐positronium. It was revealed that, at the glass transition temperature,Tg, the volume of the hole created among polymer chains expanded 1.4 times the volume at room temperature. The smaller flexural modulus of tris‐hydroxyphenylmethane than that of the other samples was explained by the volume of intermolecular‐space holes obtained from τ3. Aging effects were seen in the data of the intensities,I3, ofortho‐positronium, which became smaller after heating the samples aboveTg.I3and τ3were strongly affected by the density of cross‐linkings, and their chemical structures. The larger the density of cross‐linkings, the smallerI3and higherTgwere obtained. Epoxy compounds with the higher water‐absorption rates had larger intermolecular‐space holes. © 19

著录项

获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号