AbstractThe transport behavior of He, O2, N2, and CO2in a series of PVC/NBR polymer blends with varying acrylonitrile (AN) content in the NBR component has been studied at 25° and 50°C. In addition, measurements of density, crystallinity, and thermal expansion coefficients were carried out. The transport behavior of these blends is similar to previous result for PVC/EVA.1. With increasing AN content in NBR, the permeability (P) and diffusivity (D) of the permeants decreased while the activation energy for diffusion (ED) increased. For the polymer blends, better additivity of permeability and diffusivity was observed with increasing AN content in the NBR component. The polymer blends also showed increasing volume contraction with increasing AN content in the NBR component. These effects have been discussed as due mainly to increased polymer–polymer interaction causing reduced segmental mobility and increased compatibility of the two polymers. The sorption values calculated fromP/Dratios were largely irregular and fluctuated with the blend composition. They were less reproducible than other transport parameters, i.e.,PandDmeasured separately. Several reasons for the irregular sorption behavior were propo
展开▼