首页> 外文期刊>Corrosion: The Journal of Science and Engineering >In Situ Observations of Early Stage Oxidation of Ni-Cr and Ni-Cr-Mo Alloys
【24h】

In Situ Observations of Early Stage Oxidation of Ni-Cr and Ni-Cr-Mo Alloys

机译：In Situ Observations of Early Stage Oxidation of Ni-Cr and Ni-Cr-Mo Alloys

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相关主题

摘要

Results of in situ transmission electron microscopy experiments on the early stage oxidation of Ni-Cr and Ni-Cr-Mo alloys are reported. An epitaxial rock-salt oxide with compositions outside the conventional solubility limits initiated at the surface of both alloys, progressing by a layer-by-layer mode. Kirkendall voids were found in Ni-Cr alloys near the metal/oxide interface, but were not seen in the Ni-Cr-Mo. The voids initiated in the oxide then diffused to the metal/oxide interface, driven by the misfit stresses in the oxide. A sequential oxide initiation was observed in NiCr alloys: rock-salt - spinel - corundum; however, for NiCrMo alloys, the metastable Ni-2-xCrxO(3) (corundum structure) phase formed shortly after the growth of the rock-salt phase. Chemical analysis shows that solute atoms were captured in the initial oxide before diffusing and transforming to more thermodynamically stable phases. The results indicate that Mo doping inhibits the formation of Kirkendall voids via an increase in the nucleation rate of corundum, which was verified by density functional theory calculations.

著录项

获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号