AbstractThe kinetics of the isothermal batch macroemulsion and miniemulsion polymerizations of methyl methacrylate (MMA) at 50°C have been studied. Hexadecane was used as the cosurfactant or swelling agent. The nucleation mechanisms were observed to be different between macroemulsions and miniemulsions. The effect of surfactant, cosurfactant, initiator, shear, and hold time on droplet nucleation was studied. The miniemulsion particles were found to contain more radicals on average than the macroemulsion particles using certain recipes. This resulted in higher polymerization rates for the miniemulsions at identical particle numbers. The latex‐particle‐size distributions were similar even though the mini‐emulsion droplets start out with a high polydispersity of around 1.5. Miniemulsion latexes were found to be more stable under shear. Conductance of emulsions during polymerization was found to be a valuable on‐line tool for investigating particle nucleation and growth. © 1993 John Wiley

著录项

获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号