首页> 外文期刊>Journal of Applied Polymer Science >Morphology control of conducting polypyrrole nanostructures via operational conditions in the emulsion polymerization
【24h】

Morphology control of conducting polypyrrole nanostructures via operational conditions in the emulsion polymerization

机译：Morphology control of conducting polypyrrole nanostructures via operational conditions in the emulsion polymerization

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相关主题

摘要

Polypyrrole (PPy) nanostructures with diameter smaller than 100 nm were synthesized by chemical oxidative polymerization of pyrrole in the presence of cetyl trimethylammonium bromide and sodium dodecyl sulfate as surfactants. Hydrochloric acid was used as dopant, and a solution of potassium peroxydisulfate was used as initiator. The influence of polymerization temperature, feeding strategy, and the type of surfactant on the morphology and conductivity of PPy nanostructures were investigated and well-described. A simple route just via controlling the operational conditions in the emulsion polymerization is reported to obtain nanostructured PPy with desirable morphology and relatively good conductivity. The analysis results demonstrated that the conductivity of samples is highly affected by their morphology whereas PPy nanofibers exhibited higher conductivity respecting the other morphologies (0.66 S/cm). (C) 2017 Wiley Periodicals, Inc.

著录项

获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号