首页> 外文期刊>Solid State Communications >FP-LMTO investigations of mechanical stability and high pressure of platinum nitride compounds
【24h】

FP-LMTO investigations of mechanical stability and high pressure of platinum nitride compounds

机译：FP-LMTO investigations of mechanical stability and high pressure of platinum nitride compounds

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相关主题

摘要

We report local density functional calculations using the full potential linear muffin-tin orbital (FP-LMTO) method for binary platinum nitride (PtN), in five different crystal structures, the rock salt(B1), zinc-blende (B3), wurtzite (B4), nickel arsenide (B8), and PbS (B10) phases. The ground state properties such as the equilibrium lattice constant, elastic constants, the bulk modulus and its pressure derivative of PtN in these phases are determined and compared with the other available experimental and theoretical works. Our calculations confirm in the B3 structure that PtN is found to be mechanically stable with a large bulk modulus B = 232.45 GPa and at a sufficiently high pressure the B8(1) structure would be favoured. The theoretical transition pressure from zinc blende (B3) to NiAs (B8(1)), zinc-blende (B3) to rock-salt (B1) and zinc-blende (B3) to PbO (B10) is determined to be 9.10 GPa, 9.85 GPa and 69.35 GPa, respectively. Our calculation shows also in five different structures for PtN a high bulk modulus is a good indicator of a hard material.

著录项

获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号