首页> 外文期刊>journal of applied polymer science >Interpenetrating polymer networks from hydroxy‐terminated polybutadiene‐based polyurethanes and poly(methyl methacrylate)
【24h】

Interpenetrating polymer networks from hydroxy‐terminated polybutadiene‐based polyurethanes and poly(methyl methacrylate)

机译：Interpenetrating polymer networks from hydroxy‐terminated polybutadiene‐based polyurethanes and poly(methyl methacrylate)

获取原文
           
页面导航
  • 摘要
  • 著录项
  • 相关主题

摘要

AbstractIsocyanate‐terminated urethane prepolymer was prepared by reacting 2 mol of tolylene diisocyanate (TDI) with 1 mol of hydroxy‐terminated polybutadiene (HTPB, mol. wt. = 3000) at room temperature (30 ± 1°C) in the presence of stannous octoate as the catalyst. Urethane prepolymer was subsequently mixed with 1,4‐butane diol: glycerol (6 : 1 ratio), methyl methacrylate (MMA), and ethylene glycol dimethacrylate (EGDMA) to give an interpenetrating polymer network. Stannous octoate was used as a catalyst to give network I, and azobisisobutyronitrile (AIBN), as an initiator to give network II. Different proportions of MMA were added to the prepolymer for studying the effect of composition on mechanical properties, thermal behavior, and optical properties. The mechanothermal behavior was analyzed using a dynamic mechanical thermal analyzer. Tensile strength and modulus decreased with decreasing MMA content, whereas percent elongation at break increased. Thermal stability of the sample increased with increasing urethane content. © 1993 John WileyS

著录项

获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号