Linking Porosity to Rolling Reduction and Fatigue Lifetime of Hot Rolled AA7xxx Alloys by 3D X-Ray Computed Tomography

Xiaomin Wu; Erik Schlangen; Sybrand van der Zwaag

首页> 外文期刊>Advanced Engineering Materials >Linking Porosity to Rolling Reduction and Fatigue Lifetime of Hot Rolled AA7xxx Alloys by 3D X-Ray Computed Tomography

【24h】

Linking Porosity to Rolling Reduction and Fatigue Lifetime of Hot Rolled AA7xxx Alloys by 3D X-Ray Computed Tomography

机译：Linking Porosity to Rolling Reduction and Fatigue Lifetime of Hot Rolled AA7xxx Alloys by 3D X-Ray Computed Tomography

获取原文

获取原文并翻译 | 示例

掌桥外文数据库（机构版） >>

开具论文收录证明 >>

文献代查 >>

页面导航

摘要
著录项
相关主题

摘要

A set of hot rolled 7xxx aluminum alloys with different casting conditions and modification of processing conditions were analyzed on their fatigue life time as well as the internal microstructure using 3D computed X-ray tomography with a lab scale scanner and optical microscopy. It is shown that large retained casting pores exist in samples with low reduction rate. The modification on the hot rolling process is now proved to be much more effective on removing large casting pores in the alloy. It is also found that with the improved casting conditions and the additional deformation imposed by increased rolling reduction, this advantage is getting retarded. The combination of porosity analysis with low cycle fatigue test at peak stress of 300 MPa indicates that reduction of the size of large pores in the sample down to 10 mm will lead to greatly improved fatigue life times.

著录项

来源
《Advanced Engineering Materials》 |2012年第7期|457-463|共7页
作者
Xiaomin Wu; Erik Schlangen; Sybrand van der Zwaag;
展开▼
作者单位

Faculty of Civil Engineering and Geosciences, Delft University of Technology;

Faculty of Aerospace Engineering, Delft University of Technology;

Material Innovation Institute (M2i), Faculty of Aerospace Engineering, Delft University of Technology;

展开▼
收录信息
原文格式 PDF
正文语种英语
中图分类工程材料学;
关键词

Linking Porosity to Rolling Reduction and Fatigue Lifetime of Hot Rolled AA7xxx Alloys by 3D X-Ray Computed Tomography

摘要

著录项

相关主题

期刊订阅