首页> 外文期刊>Solid State Communications >Relaxor dielectric properties of a (Ca1.5Ti0.5)(NbTi)O-7 misplaced-displacive' cubic pyrochlore synthesised via metallorganic decomposition
【24h】

Relaxor dielectric properties of a (Ca1.5Ti0.5)(NbTi)O-7 misplaced-displacive' cubic pyrochlore synthesised via metallorganic decomposition

机译：Relaxor dielectric properties of a (Ca1.5Ti0.5)(NbTi)O-7 misplaced-displacive' cubic pyrochlore synthesised via metallorganic decomposition

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相关主题

摘要

A 'misplaced-displacive Ca1.5NbTi1.5O7 (CNT) Fd (3) over barm, cubic pyrochlore phase (a = 10.2171 angstrom) has been successfully synthesised via a metallorganic decomposition route, enabling a much lower final annealing temperature than the conventional solid state reaction route. This CNT pyrochlore has a very similar stoichiometry to the family of misplaced-displacive Bi-based cubic pyrochlores (BBCPs), except that both the cation and anion sites of the ideal A(2)B(2)O(7) pyrochlore structure type are fully occupied. Essentially identical dielectric properties of the BBCPs were found with a relatively high dielectric constant of 103 and a relatively low dielectric loss of 0.009 at 100 kHz at room temperature, as well as typical relaxor dielectric behaviour at lower temperatures. The lower temperature dielectric relaxation behaviour observed in BBCPs is thus not inextricably linked to the presence of bismuth on the ideal pyrochlore A site. This provides an important new insight into the dielectric relaxation behaviour of misplaced-displacive cubic pyrochlores. (C) 2007 Elsevier Ltd. All rights reserved.

著录项

获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号