Ni-Zn ferrite nanoparticles with composition of Ni1-xZnxFe2O4 (where x=0,0.1,0.2,0.3,0.4) were prepared by the chemical sol-gelcombustion method at low temperature with a final pH value of 7. The synthesized nanopowder can be densified at a temperature lower than 950 degrees C. X-ray diffraction results showed that the dried gels synthesized from metal nitrates and citric acid transformed directly into nano-sized ferrite particles after a combustion process in air. The Zn content has a significant influence on the electromagnetic properties such as dielectric constant (epsilon'), dielectric loss tangent (tan 3) and complex dielectric constant (epsilon"). These values decrease with increasing of zinc. It is also shown that Ni-Zn powder exhibited saturation magnetization 73 emu g-l at 950 degrees C. (c) 2007 Elsevier B.V. All rights reserved.